Rust-Oleum Noxyde Plus

A 'next generation' single pack water-based elastomeric coating based on a silane modified acrylic binder with superior adhesion and corrosion protection. The product contains anti-corrosion pigments and is lead, chromate and zinc free.

Advantages:

• Superior adhesion
• It can be applied by spray, brush and roller
• High dirt pick up resistance
• 200% elastic coat does not crack or peel
• Excellent coverage of nuts, bolts and welds
• Dry fall: saves preparation & clean up time

Recommended Uses:

On iron, steel, special alloys, galvanised and metallised iron and steel, aluminium, copper, zinc, lead, etc. as rust prevention or waterproofing. For outside and inside use. Diluted with 25% water as an adhesion primer coat on slightly or non porous substrates such as glass, smooth bricks and concrete, ceramics, tiles, etc.

Technical Data

Density (g/cm³): 1,25 Gloss Level: Satin Gloss level at 60º: 24% Solids Content in weight: 66% Solids content in volume: 46% Salt Spray Resistance: 1.248h salt spray resistance ISO 9227:2017 Drying Times Touch dry: 1hr and 20 minutes Dry to handle: 2 hours and 45 minutes Dry to recoat: 24 hours Fully cured: 2 weeks Recommended Wet Film Thickness 380 µm Recommended Dry Film Thickness 175 μm Theoretical Consumption Brush/Roller - 240 - 360 g/m²/coat Airless - 360 - 600 g/m²/coat Total consumption for optimal rust preventive protection 950 g/m² (in minimum 2 coats) = 350 µm dry film thickness