Rust-Oleum Noxyde Plus

Rust-Oleum Noxyde Plus

Single pack water-based elastomeric coating based on a silane modified acrylic binder with superior adhesion and corrosion protection. The product contains anti-corrosion pigments and is lead, chromate and zinc free.

  • Superior adhesion
  • High dirt pick up resistance
  • 200% elastic coat does not crack or peel
  • Excellent coverage of nuts, bolts and welds
  • Dry fall: saves preparation & clean up time

A ‘next generation’ single pack water-based elastomeric coating based on a silane modified acrylic binder with superior adhesion and corrosion protection. The product contains anti-corrosion pigments and is lead, chromate and zinc free.

Advantages:

  • Superior adhesion
  • It can be applied by spray, brush and roller
  • High dirt pick up resistance
  • 200% elastic coat does not crack or peel
  • Excellent coverage of nuts, bolts and welds
  • Dry fall: saves preparation & clean up time

Recommended Uses:

On iron, steel, special alloys, galvanised and metallised iron and steel, aluminium, copper, zinc, lead, etc. as rust prevention or waterproofing. For outside and inside use.

Diluted with 25% water as an adhesion primer coat on slightly or non porous substrates such as glass, smooth bricks and concrete, ceramics, tiles, etc.

Technical Data

Density (g/cm³): 1,25
Gloss Level: Satin
Gloss level at 60º: 24%
Solids Content in weight: 66%
Solids content in volume: 46%
Salt Spray Resistance: 1.248h salt spray resistance ISO 9227:2017

Drying Times
Touch dry: 1hr and 20 minutes
Dry to handle: 2 hours and 45 minutes
Dry to recoat: 24 hours
Fully cured: 2 weeks

Recommended Wet Film Thickness
380 µm

Recommended Dry Film Thickness
175 μm

Theoretical Consumption
Brush/Roller – 240 – 360 g/m²/coat
Airless – 360 – 600 g/m²/coat

Total consumption for optimal rust preventive protection 950 g/m² (in minimum 2 coats) = 350 µm dry film thickness

Download Datasheet

Reviews

There are no reviews yet.

Be the first to review “Rust-Oleum Noxyde Plus”

Your email address will not be published.

You may also like…

Rust-Oleum Noxyde

Rust-Oleum Noxyde is an anti-rust coating for roofing and cladding.

ref

WATLA

composition

87% Polivinyl | 6,5% PES | 6,5% CO

width

140

Height

100

Guard ELC – Roof and Cladding Coating

Guard ELC is a fully tint-able, one component, water-based metal roof and cladding coating with unequalled corrosion protection.

 Large U.K Stock for Fast Free Deliver

• No Primer Required

 Surface Tolerant Primer/Finish Coating

• U.V and Impact-resistant

• Anticorrosive and Waterproof

• 200% Elasticity

• Dry Fall Product

Rust-Oleum Noxyde Tape

Self adhesive butyl rubber tape for use with Noxyde.

ref

WATLA

composition

87% Polivinyl | 6,5% PES | 6,5% CO

width

140

Height

100